1. Galvanized steel plate SECC

The substrate of SECC is a general cold-rolled steel coil, which becomes an electrogalvanized product after undergoing degreasing, pickling, electroplating, and various post-treatment processes on a continuous electrogalvanizing production line. SECC not only has the mechanical properties and similar processability of ordinary cold rolled steel sheets, but also has superior corrosion resistance and decorative appearance. It has great competitiveness and substitutability in the market of electronic products, home appliances, and furniture. For example, SECC is commonly used in computer chassis.

2. Ordinary cold rolled sheet SPCC

SPCC refers to the continuous rolling of steel ingots into steel plate coils or sheets of required thickness through a cold rolling mill. The surface of SPCC lacks any protection and is easily oxidized when exposed to air, especially in humid environments where the oxidation rate accelerates and dark red rust appears. The surface needs to be painted, electroplated, or other protective measures when used.

3. Hot dip galvanized steel plate SGCC

Hot dip galvanized steel coil refers to the semi-finished product after hot rolling, acid pickling or cold rolling, which is cleaned, annealed, and immersed in a molten zinc bath at a temperature of about 460 ° C to coat the steel sheet with a zinc layer, and then subjected to quenching, tempering, leveling, and chemical treatment. SGCC material is harder than SECC material, with poor ductility (avoiding deep drawing design), thicker zinc layer, and poor weldability.

4. Stainless steel SUS304

One of the widely used stainless steels, which contains Ni (nickel), is more corrosion-resistant and heat-resistant than steel containing Cr (chromium). It has excellent mechanical properties, no heat treatment hardening phenomenon, and no elasticity.

5. Stainless steel SUS301

The content of Cr (chromium) is lower than SUS304, and its corrosion resistance is poor. However, after cold processing, it can achieve good tensile strength and hardness during stamping processing, with good elasticity. It is mainly used for spring springs and EMI prevention.